High Carbon Iron Filamet™

  • $ 78.00


High Carbon Iron Filamet™ contains around 80% metal and has a density of 2.75g/cc. Filamet™ enables any Fused Filament Fabrication printer to produce metal objects. Once fired in a sintering furnace, the result is 100% metal. High Carbon Iron Filamet™ is highly ferromagnetic both before and after sintering.

3D Printer setup: Visit our Use Instructions page for full printing, sintering and polishing guidelines.

Temperature: 205-235°C (401-455°F)
Set print bed to 40-50°C (104-122°F) (optional)

Tip: Put a layer of blue painters tape on the print bed. Our metal filament Filamet™ has great adhesion to the bed.

Speed: 30mm/sec (1800mm/min) to start.

Layer Height: Many slicers lay down an extra wide first layer to get good adhesion to the bed. This is not a problem unless the first layer is very short. With traditional PLA, it will simply squeeze out at the sides. Filamet™ is more viscous which slows this process. If the nozzle seems clogged, it may be that the nozzle is too close to the bed on the first layer. Once dialed in, some users are printing down to a layer height of 0.1mm.

Nozzle: 0.8mm or larger, standard hardened steel.

Spool Placement: Reducing friction and pull on Filamet™ during printing is important. Try hanging the filament spool just above the printer.

When sintering in a vacuum or inert environment, use Al203 and/or Powdered Graphite.

Eliminate tooling and machining costs for short run manufacturing, prototyping, and one-off metal part needs.

Note: All sales final except in cases of defective product.

Made In America